DIALEAD® Standard Grade

Continuous Fiber

Dialead Continuous Fiber

 DIALEAD® continuous fiber has excellent properties and wide range of modulus level.

  [ standard grade ](Continuous Fiber)
  Grade Tensile
Modulus
[GPa]		 Tensile
Strength
[MPa]		 Elongation
[%]		 Density
[g/cm3]		 Yield
[g/1000m]		 Thermal
Conductivity
[W/m·K]
2K type K1352U 620 3,600 0.6 2.12 270 140
K1392U 760 3,700 0.5 2.15 270 210
K13C2U 900 3,800 0.4 2.20 270 620
K13D2U 935 3,700 0.4 2.21 365 800
12K type K63712 640 2,600 0.4 2.12 2,000 140
K63A12 790 2,600 0.3 2.15 1,950 220
This information can be used for material selection only.
[ Laminate Properties ] (2K)
Style:Uni-directional [0]t
Resin:FIBERITE 934
K1352U K1392U K13C2U K13D2U  
Longitudinal tensile strength [MPa] 2,000 2,100 2,200 1.800 ASTM D3039
Modulus [GPa] 380 460 560 560
Compressive strength [MPa] 450 400 380 340 ASTM D3410
Modulus [GPa] 250 420 560 560
ILSS [MPa] 75 70 50 40 ASTM D2344
CTE(Tmep. 50-125°C) [x10-6·K] -1.1 -1.2 -1.2 -1.2  
Tranverse tensile strength [MPa] 40 35 30 25  
Modulus [GPa] 6.2 6.0 5.4 5.1  
Data are average results of experiments made on standard procedures and subject to normal manufacturing variation.
Tensile and compressive data normalized by 60% Fiber volume.
[ Laminate Properties ] (12K)
Style:Uni-directional [0]t
Resin:250°F Cure Epoxy
K63712 K63A12  
Longitudinal tensile strength [MPa] 1,500 1,500 ASTM D3039
Modulus [GPa] 370 470
Compressive strength [MPa] 440 380 ASTM D3410
Modulus [GPa] 330 470
ILSS [MPa] 75 70 ASTM D2344
CTE(Tmep. 50-125°C) [x10-6·K] -1.1 -1.2  
Tranverse tensile strength [MPa] 35 26  
Modulus [GPa] 5.4 5.2  
Data are average results of experiments made on standard procedures and subject to normal manufacturing variation.
Tensile and compressive data normalized by 60% Fiber volume.

Chopped Fiber

Dialead Chopped Fiber

 DIALEAD® chopped fibers are available to meet the demands of higher Electric Conductivity, Thermal Conductivity and Mechanical Properties.

[ standard grade ] (Chopper Fiber)
Grade Tensile
Modulus
[GPa]		 Tensile
Strength
[MPa]		 Elongation
[%]		 Density
[g/cm3]		 Thermal
Conductivity
[W/m·K]
K223Y1 50 1,000 1.8 1.5 -
K223SE 185 2,350 1.1 2.0 -
K223QG 590 3,230 0.6 2.1 140
K223HG 900 3,800 0.3 2.2 540
K223HE 900 3,800 0.3 2.2 550
K6371T 640 2,600 0.4 2.2 140
This information can be used for material selection only.
[ Fiber Properties ]
  K223SE K223Y1 K223QE K223QG K223HG K223HE K6371T
Bulk properties Length [mm] 6 6 6 6 6 6 6
Bulk density [g/l] >400 >400 >400 >400 >400 >400 >400
Shape   round round round round round round flat
Sizing Amount [%] 4 - 6 4 - 6 0 0 0 0 1 - 3
Filament properties Filament Dia. [µm] 11 13 11 11 11 11 11
T.C. [W/m·K] 20 <5 20 140 540 550 140
T.Modulus [GPa] 185 50 185 590 900 900 640
T.Strength [MPa] 2,350 1,000 2,350 3,230 3,800 3,800 2,600
Elongation [%] 1.1 1.8 1.1 0.6 0.3 0.3 0.4
Density [g/cm3] 2.0 1.5 2.0 2.1 2.2 2.2 2.1
This information can be used for material selection only.
[ Target Resin ]
·General Resin : ABS, PP etc...
·Engineering Plastic : PC, POM, mPPO, PBT, PA, LCP, PPS, PES, PEEK, PEI etc...

Milled Fiber

 DIALEAD® is available in milled fibers. Our milled products retain good properties to achieve high performance.

[ standard grade ] (Milled Fiber)
Grade Tensile
Modulus
[GPa]		 Tensile
Strength
[MPa]		 Elongation
[g/cm3]		 Thermal
Conductivity
[W/m·K]		 Fiber Length
[average]		 Sizing
Amount
[%]
K223QM 590 3,230 2.1 140 50µm 0
K6371M 640 2,600 2.1 140 50µm 1 - 3
K223HM 900 3,800 2.2 550 50µm,200µm 0
This information can be used for material selection only.

Fabric

Dialead Fabric

 DIALEAD® continuous fiber has excellent properties and wide range of modulus level.

Numerous area weights and weave patterns are available.
[ Typical grade ] (Fabric)
Grade Style FAW
[g/m2]		 DIALEAD
Grade
FP3A107 plain 75 K13A1L
FT3C244 plain 400 K13C2U